PPS GDX310-65BK玻纤矿物增强聚苯硫醚
Glass Fiber and Mineral Reinforced Polyphenylene Sulfide
产品特性
PPS GDX310-65BK是一种含65%玻璃纤维和矿物增强的聚苯硫醚材料，具备优良的力学性能、耐化学腐蚀性能以及耐热性能
PPS GDX310-65BK is a 65% glass fiber and mineral reinforced polyphenylene sulfide material with excellent mechanical properties, chemical corrosion resistance and heat resistance.
产品用途
本品主要用于智能信息终端，智能家居、家电，智能汽车，智能交通以及智能城市等广泛应用领域；可制造5G通讯设备终端壳体和包覆、防护材料，工业自动化、远程医疗、自动驾驶的仪器与设备的壳体与框架材料等
This product is mainly used in a wide range of applications such as smart information terminals, smart homes, home appliances, smart cars, smart transportation and smart cities; it can manufacture terminal shells and coatings for 5G communication equipment, protective materials, industrial automation, telemedicine, and autonomous driving The shell and frame material of the instruments and equipment
物理性能 单位 测试标准 测试结果
Physical Property unit Testing Standard Test Result
密度 g/cm3 ISO 1183 1.98
Density
成型收缩率-平行流动方向 % ISO 294-4 0.2
Molding shrinkage-Parallel flow
成型收缩率-垂直流动方向 % ISO 294-4 0.6
Molding shrinkage-Vertical flow
吸水率（23℃,24Hrs） % ISO 62 0.02
Water absorption rate
机械性能 单位 测试标准 测试结果
Mechanical Property unit Testing Standard Test Result
拉伸强度 MPa ISO 527 135.0
Tensile Strength
弯曲强度 MPa ISO 178 225.0
Flexural Strength
弯曲模量 GPa ISO 178 21.5
Flexural Modulus
简支梁无缺口冲击强度 kJ/m2 ISO 179 25.0
Charpy Impact Strength
简支梁缺口冲击强度 kJ/m2 ISO 179 6.5
Charpy Notched Impact Strength
热性能 单位 测试标准 测试结果
Thermal property unit Testing Standard Test Result
熔点 ℃ ISO 11357 285.0
Melting Point
热变形温度(1.8MPa) ℃ ISO 75 265.0
Hot Deformation Temperature
阻燃性 UL-94 V-0
Flame Retardancy
注塑成型条件 单位 参考值
Injection Molding Conditions unit Reference Value
烘料温度
Drying Tmperature
烘料时间
Drying Time
筒体加热温度
Heating temperature of cylinder
射嘴温度
Nozzle Temperature
模具温度
Mold Temperature
注射压力
Injection Pressure
保压压力
Packing Pressure
℃ 130-150
Hrs 3-4
℃ 290-320
℃ 300-320
℃ 130-150
Mpa 80-150
Mpa 30-70