| 规格级别： | 耐蒸汽级 | 外观颜色： | — |
| 用途概述： | 眼药容器、角腊接触镜片盒、人造肾 | ||
| 备注说明： | 特性：提高了耐水解性 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | — | ASTM D-792 | 1.20 | — |
| 吸水率 | 23℃，24时间 | ASTM D-570 | 0.23 | % | |
| 光线透过率 | 3mm | ASTM D-1003 | 85～89 | % | |
| 熔体流动速率 | 300℃ | ISO 1133 | 12 | g/10min | |
| 机械性能 | 拉伸强度 | — | ASTM D-638 | 64 | MPa |
| 拉伸强度 | — | ASTM D-638 | 68 | MPa | |
| 拉伸模量 | — | ASTM D-638 | 2300 | MPa | |
| 断裂伸长率 | — | ASTM D-638 | 115 | % | |
| 挠曲强度 | — | ASTM D-790 | 93 | MPa | |
| 弯曲模量 | — | ASTM D-790 | 2350 | MPa | |
| IZOD缺口冲击强度 | — | ASTM D-256 | 70 | KJ/m2 | |
| 洛氏硬度 | — | ASTM D-785 | R-120 | — | |
| 塔泊磨损 | — | ASTM D-1044 | 12 | Mg | |
| 电气性能 | 绝缘破坏电压 | 1.6mm | ASTM D-149 | 30 | Kv/mm |
| 体积固有抵抗 | — | ASTM D-257 | 1016< | Ω.cm | |
| 介电常数 | 60HZ | ASTM D-150 | 2.91 | — | |
| 介电耗损正接 | 60HZ | ASTM D-150 | 6.6×10-4 | — | |
| 抗电弧 | — | ASTM D-495 | 110 | SEc | |
| 热 性 能 | 成型收缩率 | — | ASTM D-955 | 0.5-0.7 | % |
| 阻燃性 | 1.47mm | UL 94 | V-2 | — | |
| 负荷挠曲温度 | 1.8MPa | ASTM D-648 | 132 | ℃ | |
| 维卡软化温度 | — | ISO 306 | 148 | ℃ | |
| 线膨胀系数 | — | ASTM D-696 | 6.5 | ×10-5 | |
比重:1.18-1.20克/立方厘米 成型收缩率:0.5-0.8%
成型温度：230-320℃
干燥条件：110-120℃ 8小时 可在 -60~120℃下长期使用
物料性能 冲击强度高，尺寸稳定性好，无色透明，着色性好，电绝缘性、耐腐蚀性、耐磨性好，但自润滑性差，有应力开裂倾向，高温易水解，与其它树脂相溶性差。
适于制作仪表小零件、绝缘透明件和耐冲击零件