PLEXIMID® TT50 is a highly heat distortion-resistant poly(n-methyl methacrylimide) (PMMI).
Besides showing the properties common to all PLEXIMID® molding compounds, such as
high heat deflection temperature under load,
excellent transmission and clarity,
very high strength and rigidity, as well as
good weather resistance.
PLEXIMID® TT50 is special in that it is
listed by AMECA.
Application:
PLEXIMID® molding compound is particularly suitable for injection molding of items meant for applications that involve high heat loads.
| 总览 | |
| 材料状态 |
已商用：当前有效
|
| 资料 1 | |
| UL 黄卡 2 | |
| 搜索 UL 黄卡 | |
| 供货地区 |
欧洲
|
| 特性 |
高刚性
高强度
高透過率
耐候性，良好
耐热性，高
清晰度，高
|
| 用途 |
光纤电缆
镜头
汽车领域的应用
照明应用
|
| 形式 |
粒子
|
| 加工方法 |
注射成型
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
| 密度 |
1.21
|
g/cm³
|
ISO 1183 |
| 熔流率（熔体流动速率） (260°C/10.0 kg) |
5.0
|
g/10 min
|
ISO 1133 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
| 拉伸模量 |
4000
|
MPa
|
ISO 527-1/1 |
| 拉伸应力 (断裂) |
80.0
|
MPa
|
ISO 527-2/5 |
| 拉伸应变 (断裂) |
3.0
|
%
|
ISO 527-2/5 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
| 简支梁无缺口冲击强度 (23°C) |
20
|
kJ/m²
|
ISO 179/1eU |
| 热性能 |
额定值
|
单位制
|
测试方法
|
| 载荷下热变形温度 | |||
| 0.45 MPa, 未退火 |
140
|
°C
|
ISO 75-2/B |
| 1.8 MPa, 未退火 |
132
|
°C
|
ISO 75-2/A |
| 维卡软化温度 |
150
|
°C
|
ISO 306/B50 |
| 线形热膨胀系数 – 流动 (0 到 50°C) |
5.3E-5
|
cm/cm/°C
|
ISO 11359-2 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
| 可燃性等级 (1.5 mm) |
HB
|
IEC 60695-11-10, -20 |
| 光学性能 |
额定值
|
单位制
|
测试方法
|
| 折射率 4 |
1.530
|
ISO 489 | |
| 透射率 5 (3000 µm) |
91.0
|
%
|
ISO 13468-2 |
| 注射 |
额定值
|
单位制
|
|
| 干燥温度 – 热风干燥机 |
< 100
|
°C
|
|
| 干燥时间 |
2.0 到 3.0
|
hr
|
|
| 加工（熔体）温度 |
250 到 280
|
°C
|
|
| 模具温度 |
110
|
°C
|