TYPICAL PROPERTIES (1) |
||||
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress, yld, Type I, 50 mm/min |
590 |
kgf/cm² |
ASTM D 638 |
|
Tensile Stress, brk, Type I, 50 mm/min |
580 |
kgf/cm² |
ASTM D 638 |
|
Tensile Strain, yld, Type I, 50 mm/min |
5.7 |
% |
ASTM D 638 |
|
Tensile Strain, brk, Type I, 50 mm/min |
117.9 |
% |
ASTM D 638 |
|
Tensile Modulus, 50 mm/min |
23000 |
kgf/cm² |
ASTM D 638 |
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span |
960 |
kgf/cm² |
ASTM D 790 |
|
Flexural Modulus, 1.3 mm/min, 50 mm span |
22900 |
kgf/cm² |
ASTM D 790 |
|
Tensile Stress, yield, 50 mm/min |
57 |
MPa |
ISO 527 |
|
Tensile Stress, break, 50 mm/min |
56 |
MPa |
ISO 527 |
|
Tensile Strain, yield, 50 mm/min |
5.4 |
% |
ISO 527 |
|
Tensile Strain, break, 50 mm/min |
119.4 |
% |
ISO 527 |
|
Tensile Modulus, 1 mm/min |
2340 |
MPa |
ISO 527 |
|
Flexural Stress, yield, 2 mm/min |
89 |
MPa |
ISO 178 |
|
Flexural Modulus, 2 mm/min |
2140 |
MPa |
ISO 178 |
|
Hardness, Rockwell L |
89 |
- |
ISO 2039-2 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact, notched, 23°C |
75 |
cm-kgf/cm |
ASTM D 256 |
|
Izod Impact, notched, -30°C |
63 |
cm-kgf/cm |
ASTM D 256 |
|
Instrumented Impact Total Energy, 23°C |
763 |
cm-kgf |
ASTM D 3763 |
|
Izod Impact, unnotched 80*10*3 +23°C |
NB |
kJ/m² |
ISO 180/1U |
|
Izod Impact, unnotched 80*10*3 -30°C |
NB |
kJ/m² |
ISO 180/1U |
|
Izod Impact, notched 80*10*3 +23°C |
55 |
kJ/m² |
ISO 180/1A |
|
Izod Impact, notched 80*10*3 -30°C |
40 |
kJ/m² |
ISO 180/1A |
|
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm |
65 |
kJ/m² |
ISO 179/1eA |
|
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm |
45 |
kJ/m² |
ISO 179/1eA |
|
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm |
NB |
kJ/m² |
ISO 179/1eU |
|
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm |
NB |
kJ/m² |
ISO 179/1eU |
|
THERMAL |
Value |
Unit |
Standard |
|
Vicat Softening Temp, Rate A/50 |
138 |
°C |
ASTM D 1525 |
|
HDT, 1.82 MPa, 3.2mm, unannealed |
121 |
°C |
ASTM D 648 |
|
CTE, -40°C to 95°C, flow |
7.48E-05 |
1/°C |
ASTM E 831 |
|
CTE, -40°C to 95°C, xflow |
7.64E-05 |
1/°C |
ASTM E 831 |
|
CTE, 23°C to 80°C, flow |
7.48E-05 |
1/°C |
ISO 11359-2 |
|
CTE, 23°C to 80°C, xflow |
7.64E-05 |
1/°C |
ISO 11359-2 |
|
Ball Pressure Test, 125°C +/- 2°C |
pass |
- |
IEC 60695-10-2 |
|
Vicat Softening Temp, Rate B/50 |
138 |
°C |
ISO 306 |
|
Vicat Softening Temp, Rate B/120 |
139 |
°C |
ISO 306 |
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
116 |
°C |
ISO 75/Af |
|
Relative Temp Index, Elec |
130 |
°C |
UL 746B |
|
Relative Temp Index, Mech w/o impact |
130 |
°C |
UL 746B |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Specific Gravity |
1.19 |
- |
ASTM D 792 |
|
Mold Shrinkage, flow, 3.2 mm (5) |
0.4 – 0.8 |
% |
Method |
|
Mold Shrinkage, xflow, 3.2 mm (5) |
0.4 – 0.8 |
% |
SABIC Method |
|
Melt Flow Rate, 300°C/1.2 kgf |
20 |
g/10 min |
ASTM D 1238 |
|
Density |
1.19 |
g/cm³ |
ISO 1183 |
|
Water Absorption, (23°C/sat) |
0.12 |
% |
ISO 62 |
|
Moisture Absorption (23°C / 50% RH) |
0.09 |
% |
ISO 62 |
|
Melt Volume Rate, MVR at 300°C/1.2 kg |
19 |
cm³/10 min |
ISO 1133 |
|
OPTICAL |
Value |
Unit |
Standard |
|
Light Transmission, 2.54 mm |
82 |
% |
ASTM D 1003 |
|
Haze, 2.54 mm |
3 |
% |
ASTM D 1003 |
|
ELECTRICAL |
Value |
Unit |
Standard |
|
Volume Resistivity |
>1.E+15 |
Ohm-cm |
ASTM D 257 |
|
Surface Resistivity |
>1.E+15 |
Ohm |
ASTM D 257 |
|
FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
|
UL Recognized, 94HB Flame Class Rating (3) |
1.5 |
mm |
UL 94 |
|
Glow Wire Flammability Index 960°C, passes at |
3 |
mm |
IEC 60695-2-12 |
|
Glow Wire Ignitability Temperature, 0.8 mm |
850 |
°C |
IEC 60695-2-13 |
|
Glow Wire Ignitability Temperature, 3.0 mm |
850 |
°C |
IEC 60695-2-13 |
|
Source GMD, last updated:2004/09/17 |
|
Parameter |
||
Injection Molding |
Value |
Unit |
Drying Temperature |
120 |
°C |
Drying Time |
3 – 4 |
hrs |
Drying Time (Cumulative) |
48 |
hrs |
Maximum Moisture Content |
0.02 |
% |
Melt Temperature |
295 – 315 |
°C |
Nozzle Temperature |
290 – 310 |
°C |
Front – Zone 3 Temperature |
295 – 315 |
°C |
Middle – Zone 2 Temperature |
280 – 305 |
°C |
Rear – Zone 1 Temperature |
215 – 295 |
°C |
Mold Temperature |
70 – 95 |
°C |
Back Pressure |
0.3 – 0.7 |
MPa |
Screw Speed |
40 – 70 |
rpm |
Shot to Cylinder Size |
40 – 60 |
% |
Vent Depth |
0.025 – 0.076 |
mm |
ource GMD, last updated:2004/09/17 |