PC-301-10/美国陶氏
①原料描述部分
|
规格级别 |
注塑 |
外观颜色 |
|
|
该料用途 |
|
||
|
备注说明 |
特性：脱模良好，中粘度 |
||
②加工条件
|
加工条件 |
|
|
③原料技术数据
|
性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
||
|
基本性能 |
平衡吸水率 |
23℃，相对湿度50% |
ASTM D-570 |
0.32 |
% |
|
|
熔体流动速率 |
300℃/1.2kg |
ASTM D-1238 |
10 |
g/10min |
||
|
吸水率 |
24hr,23℃ |
ASTM D-570 |
0.15 |
% |
||
|
物理性能 |
阻燃等级 |
1.6mm |
UL 94 |
HB |
|
|
|
透光率 |
|
ASTM D-1003 |
89 |
% |
||
|
折射率 |
|
ASTM D-542 |
1.586 |
|
||
|
模具收缩率 |
|
ASTM D-955 |
0.005-0.007 |
in/in |
||
|
阻燃等级 |
3.2mm |
UL 94 |
HB |
|
||
|
比重 |
|
ASTM D-792 |
1200 |
kg/m3 |
||
|
雾度 |
|
ASTM D-1003 |
0.7-1.5 |
% |
||
|
机械性能 |
拉伸模量 |
|
ASTM D-638 |
2410 |
MPa |
|
|
落锤冲击强度 |
总能量@23℃ |
ASTM D-3763 |
87 |
J |
||
|
冲击强度 |
23℃ |
ASTM D-256 |
未破裂 |
|
||
|
弯曲强度 |
|
ASTM D-790 |
96 |
MPa |
||
|
拉伸强度 |
屈服点 |
50mm/min |
ASTM D-638 |
60 |
MPa |
|
|
断裂点 |
- |
ASTM D-638 |
71 |
MPa |
||
|
洛氏硬度 |
|
ASTM D-785 |
118 |
R标度 |
||
|
洛氏硬度 |
|
ASTM D-785 |
73 |
M标度 |
||
|
缺口冲击强度 |
23℃ |
ASTM D-256 |
900 |
j/m |
||
|
伸长率 |
屈服点 |
|
ASTM D-638 |
6 |
% |
|
|
断裂点 |
|
ASTM D-638 |
150 |
% |
||
|
弯曲模量 |
|
ASTM D-790 |
2410 |
MPa |
||
|
电气性能 |
介电强度 |
60Hz |
ASTM D-149 |
17 |
V/mil |
|
|
辉光灯丝测试 |
2mm，5s |
IEC 695-2-1 |
850 |
℃ |
||
|
体积电阻 |
23℃，干 |
ASTM D-257 |
2.0×1017 |
Ω.cm |
||
|
损耗因素 |
60Hz |
ASTM D-150 |
0.001 |
|
||
|
球状压痕温度 |
|
IEC 598-1 |
>125 |
℃ |
||
|
对比电弧径迹指数 |
2mm |
IEC 112 |
250 |
V |
||
|
热性能 |
热变形温度 |
未退火@1.82MPa |
ASTM D-648 |
128 |
℃ |
|
|
热变形温度 |
退火@1.82MPa |
ASTM D-648 |
141 |
℃ |
||
|
平均燃烧系数 |
|
ASTM D-635 |
25 |
mm |
||
|
维卡软化点 |
50℃/小时，50n重 |
ASTM D-1525 |
149 |
℃ |
||
|
线性热收缩率 |
-40℃～82℃ |
ASTM D-696 |
68×10-6 |
mm/mm/℃ |
||
|
热变形温度 |
退火@0.45MPa |
ASTM D-648 |
144 |
℃ |
||
|
其它性能 |
需氧系数 |
|
ASTM D-2863 |
26 |
% |
|