PBT台湾长春5130-104- 生产企业： 台湾长春
| 规格级别 | 增强,纤维 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 吸湿率 | 24h | ASTM D570 | 0.03 | % | |
| 玻璃纤维含量 | 30 | % | ||||
| 比重 | ASTM D792 | 1.54 | ||||
| 机械性能 | 硬度 | ASTM D785 | 90 | M | ||
| 引张伸长率 | ASTM D638 | 3.0 | % | |||
| 挠曲模数 | ASTM D790 | 3.0 | kg/cm2 | |||
| 挠曲强度 | ASTM D790 | 1800 | kg/cm2 | |||
| 挠曲强度 | ASTM D790 | 1800 | kg/cm2 | |||
| 挠曲强度 | ASTM D790 | 1800 | kg/cm2 | |||
| 引张强度 | ASTM D638 | 580 | kg/cm2 | |||
| 冲击强度 | ASTM D256 | 7 | kg.cm/cm | |||
| 挠曲模数 | ASTM D790 | 88000 | kg/cm2 | |||
| 电气性能 | 体积抵抗率 | ASTM D257 | 1015 | Ω.cm | ||
| CTI | IEC 112 | 175～250V | V | |||
| 诱电正接 | ASTM D150 | 0.01 | 60Hz | |||
| 介电常数 | ASTM D150 | 3.2 | 60Hz | |||
| 耐电弧性 | ASTM D495 | 110 | SEC | |||
| 绝缘破坏强度 | 2mm | ASTM D149 | 19 | KV/mm | ||
| 表面抵抗率 | ASTM D257 | 1013 | Ω | |||
| 热性能 | 热膨胀系数 | ASTM D696 | 3 | 10-5cm/cm℃ | ||
| 热变形温度 | - | 18.6kg/cm2 | ASTM D648 | 195 | ℃ | |
| - | 4.6kg/cm2 | ASTM D648 | 210 | ℃ | ||
| 熔点 | DSC | 225 | ℃ | |||
| 耐燃性 | 0.8mm | UL94 | V-0 | |||
☆PBT的耐磨性能：PBT本身磨擦因子小，仅大于氟类塑料且与共聚甲醛差不多，其磨耗量比PC、POM还小。
☆PBT的吸水性：PBT树脂在空气中的饱和吸水率均小于0.10%，同玻璃纤维增强尼龙0.65%（未饱和）相比非常小。在室温的水中放置100小时，吸水率是0.22%，150小时是0.28%，比玻璃纤维增强尼龙的吸水率4.8%（未饱和）小得多。因此，因吸湿的尺寸变化可忽略不计。
☆PBT的易成型性：由于流动性好，结晶速度快，加工制件所需的生产周期只需几秒到几十秒。
☆PBT的尺寸稳定性：在使用过程中的尺寸变化非常小，成型稳定性和尺寸精度方面非常优良。
☆PBT的缺陷：①会受到沸水影响，当长时间浸泡高温热水中，其大分子会发生水解，导致相对分子质量下降，使聚合度和强度均下降，所以使用时必须注意。若在低于60℃的热水中，可长期连续使用。②部份溶剂对PBT有侵蚀，会被芳烃、醋酸、醋酸乙酯溶胀；强酸、强碱和苯酚可以使PBT破裂。